Description
| Item | FH-140 | FN-130 | FLN-130 | MS-1 | FL-S | XA-1 | XA-2 | |
|---|---|---|---|---|---|---|---|---|
| Chemical composition, % | Al2O3 | ≥45 | ≥40 | ≥35 | ≥50 | - | ≥60 | ≥70 |
| CaO | - | - | - | ≥0.5 | - | - | - | |
| MgO | - | - | - | - | - | - | - | |
| Refractoriness, ℃ | ≥1610 | ≥1530 | - | ≥1530 | - | ≥1730 | ≥1790 | |
| Density, g/cm3, ℃×3h | 1400℃×3h ≥1.9 | 1400℃×3h ≥1.65 | 1300℃×3h ≥1.4 | 1300℃×3h ≥2.1 | 1100℃×3h ≥1.3 | 1300℃×3h ≥2.3 | 1300℃×3h ≥2.5 |
|
| Crushing strength, MPa | ≥24 | ≥19 | ≥14 | - | - | ≥39 | ≥30 | |
| Modulus of rupture | 110℃×24h | ≥5.5 | ≥3.5 | ≥2.5 | ≥2.9 | ≥1.4 | ≥6.5 | ≥3.5 |
| Hot state | 1400℃ ≥0.98 | 1300℃ ≥0.98 | 1400℃ ≥0.45 | 1400℃ ≥0.98 | after acid treatment ≥1.9 | after acid treatment ≥1.9 | 1300℃ ≥0.8 |
|
| Permanent linear change | 1400℃×3h ±1.0 | 1300℃×3h ±1.0 | 1300℃×3h ±1.0 | 1300℃×3h ±1.1 | 800℃×3h ±1.0 | 1300℃×3h ≥1.0 | 1300℃×3h ≥1.0 |
|
| Thermal conductivity W/(m·K) | - | 1300℃ 0.5-0.7 | 350℃ 0.25-0.4 | - | 350℃ ≥0.27 | - | - | |